Stainless Steel Circle

Dimensions

ASTM, ASME, API

Sizes (Seamless)

1/2″ NB upto 8″ NB

SIzes (ERW)

1/2″ NB upto 24″ NB

Sizes (EFW)

6″ NB upto 100″ NB

Wall Thickness

Schedule 5S to XXS

End

Beveled End, Plain End, Treaded

Length

Double Random, Single Random, Cut Length.

Materials Testing

H2 SERVICE, NACE MR0175, CRYO SERVICE, OXYGEN SERVICE, etc

Processing

Polishing, Cut-to-length, Polished Grit 120 to 600

Grade

C

Mn

Si

P

S

Cr

Mo

Ni

N

SS 304

0.08 max

2 max

0.75 max

0.040 max

0.030 max

18 – 20

–

8 – 11

–

Density

Melting Point

Tensile Strength

Yield Strength (0.2%Offset)

Elongation

8.0 g/cm3

1400 °C (2550 °F)

Psi – 75000 , MPa – 515

Psi – 30000 , MPa – 205

35 %

STANDARD

WERKSTOFF NR.

UNS

JIS

BS

GOST

AFNOR

EN

SS 304

1.4301

S30400

SUS 304

304S31

08??18??10

Z7CN18???09

X5CrNi18-10

Grade

Titanium Astm F136 GR5

Titanium Ams 4928 GR5

Titanium Astm B348 GR5

Common Trade Names

Grade 5 Titanium, Ti-6al-4v, 6Al-4V Titanium- UNS R56400

Standard

ASTM B348, ASTM F136, ASTM F67, ASTM F136, ISO-5832-2(3), AMS4928, MIL-T-9047G, JIS etc

Specification

AMS 4928, AMS 6931, AMS-T-9047 (6AL-4V), ASTM B348 (Grade 5), and MIL-T-9047 (6AL-4V).

Standard

ASTM, ASME, API, GB, AISI, DIN, EN, SUS, UNS

Titanium Grade 5 Round bar size

Diameter: 3-~800mm

ASTM B348 Grade 5 Titanium Section

3.0 to 12.0mm thickness

3.7165 Grade 5 Titanium Billet Size

1/2" to 495mm Diameter

ASTM B348 Gr 5 Titanium Rectangles Size

33 x 30mm to 295 x 1066mm

Gr 5 Titanium Round Bar Finish

Cold (bright) drawn, centreless ground, hot rolled, smooth turned, peeled, slit rolled edge, hot rolled annealed, Rough Turned, Bright, Polish, Grinding, Centreless Ground & Black

ASTM B348 Ti Grade 5 Round Bar Surface

Bright, Hot Rolled Pickled, Cold Drawn, Sand Blasting Finished, Polished, Hairline

Grade 5 Titanium round bar Condition

Hardened & tempered, annealed

Gr 5 Titanium Bar Technique

Hot Rolled, Cold Drawn, Cold Rolled, Forged Round Bar, Rod

Grade 5 Titanium Din 3.7165 Round Bar Tolerance

H8, H9, H10, H11, H12, H13K9, K10, K11, K12 or as per clients’ requirements

UNS R56400 Titanium Bar Processing

Bar cutting to 650mm

Element

Density

Melting Point

Tensile Strength

Yield Strength (0.2%Offset)

Elongation

Titanium Gr. 2

4.5 g/cm3

1665 °C (3030 °F)

Psi – 49900 , MPa – 344

Psi – 39900 , MPa – 275

20 %

Gr3

50

40

14.9

103 GPa

0.34-0.10

Titanium Gr. 5

4.43 g/cm3

1632 °C (2970 °F)

Psi – 138000 , MPa – 950

Psi – 128000 , MPa – 880

14 %

Ti Gr7

4.43 g/cm3

1632 °C (2970 °F)

Psi – 138000 , MPa – 950

Psi – 128000 , MPa – 880

14 %