New Items

Grade

C

Mn

Si

P

S

Cr

Mo

Ni

N

SS 304

0.08 max

2 max

0.75 max

0.040 max

0.030 max

18 – 20

–

8 – 11

–

Density

Melting Point

Tensile Strength

Yield Strength (0.2%Offset)

Elongation

8.0 g/cm3

1400 °C (2550 °F)

Psi – 75000 , MPa – 515

Psi – 30000 , MPa – 205

35 %

STANDARD

WERKSTOFF NR.

UNS

JIS

BS

GOST

AFNOR

EN

SS 304

1.4301

S30400

SUS 304

304S31

08??18??10

Z7CN18???09

X5CrNi18-10

Specifications

ASTM A240 / ASME SA240

Width

1000mm / 1219mm /1250mm / 1500mm / 2000mm

Length

2000 mm / 2440 mm / 2500 mm / 3000 mm / 6000 mm

Thickness

0.1mm to 12 mm Thk

Hardness

Soft, Hard, Half Hard, Quarter Hard, Spring Hard etc.

Finish

Hot rolled plate (HR), Cold rolled sheet (CR), 2B, 2D, BA NO(8), SATIN (Met with Plastic Coated)

Form

Coils, Foils, Rolls, Plain Sheet, Strip, Flats, Blank (Circle), Ring (Flange) etc.

Grade

C

Mn

Si

P

S

Cr

Mo

SS 416

0.15 max

1.25 max

1 max

0.06 max

0.15 min

12 – 14

0.6

SS 440

0.20 max

1.00 max

1.00 max

0.040 max

0.030 max

15.00 – 17.00

-

SS 446

0.2 max

1.5 max

0.75 max

0.04 max

0.030 max

23 – 30

–

STANDARD

Density

Tensile Strength

Yield Strength (0.2%Offset)

Elongation

SS416

7800 g/cm3

517 MPa

275 MPa

30

SS440C

7.8 g/cm3

MPa – 380

MPa – 170

20%

SS446

7.5 g/cm3

Psi – 75,000 , MPa – 485

Psi – 40,000 , MPa – 275

20%

STANDARD

WERKSTOFF NR.

UNS

JIS

BS

EN

SS416

1.4005

S41600

SUS 416

416S21

56AM

SS440C

1.4057

S44000

SUS 440

-

-

SS446

1.4762

S44600

-

-

-

Stainless Steel 416 Plain Sheets

416 Stainless Steel Shim Sheets

Stainless Steel 416 Perforated Sheet

416 Stainless Steel Galvanized Plates

Stainless Steel 416 Hot Rolled Sheets

416 Stainless Steel Cold Rolled Sheets

Grade

C

Mn

Si

P

S

Cr

Mo

Ni

N

Stainless Steel 303

0.15 max

2 max

1 max

0.20 max

0.15 min

17.0-19.0

–

8 – 10

STANDARD

WERKSTOFF NR.

UNS

JIS

BS

GOST

AFNOR

EN

Stainless Steel 303

1.4305

S30300

SUS 303

STANDARD

UNS

WERKSTOFF NR.

SS 303

S30300

1.4305

Element

Density, lb/in3

Modulus of Elasticity, psi

Linear Expansion, 68-212°F, /°F

Thermal Conductivity, Btu/ft hr°F

Heat Capacity, Btu/lb°F

Electrical Resistivity, Ω-inch

SS 303

0.285

29 x 106

9.4 x 10-6

8.7

0.12

27.6 x 10-6

Grade

WERKSTOFF NR.

UNS

AFNOR

BS

JIS

SS 409

1.4512

S40900

Z3CT12

409 S 19

SUS 409

SS 409L

1.4512

S40903

–

–

SUS 409L

SS 409M

–

S40920

–

HYFAB 3/12

SUS 409M

SS 410

1.4006

S41000

-

410S21

SUS 410

SS 430

BF Z 3 CN 19-09

-

Grades

C

Ni

Si

S

Mn

P

Cr

Ti

SS 409

0.08

0.5

1.00

0.045

1.00

0.045

11.75 -10.5<

0.75-6x C

SS 409L

0.03

0.5

1.00

0.02

1.00

0.04

11.75-10.5

0.75-6(C+N)

SS 409M

0.03

1.00

0.5-1.5

10.80-12.50

1.5 max

0.040

0.030

0.03

Grades

Density

Melting Point

Tensile Strength

Yield Strength (0.2%Offset)

Elongation

Hardness (Brinell) MAX

Hardness (Rockwell B) MAX

SS 409

8.0 g/cm3

1457 °C (2650 °F)

Psi – 75000 , MPa – 515

Psi – 30000 , MPa – 205

35 %

SS 409L

8.0 g/cm3

1457 °C (2650 °F)

Psi – 75000 , MPa – 515

Psi – 30000 , MPa – 205

35 %

STANDARD

WERKSTOFF NR.

UNS

Nitronic 50

1.3964

S20910

Nitronic 60

S21800

-

Grade

C

Mn

Si

P

S

Cr

Mo

Ni

Nitronic 50

0.06 max

4.0-6.0 max

1.00 max

0.045 max

0.030 max

23.5

3.00

13.5

Nitronic 60

min.

-

7.00

3.5

-

-

16.00

-

8.00

max.

0.10

9.00

4.5

-

-

18.00

0.75

9.00

Grade

Tensile Strength (ksi) min

Elongation (% in 50mm) min

Yield Strength 0.2% Proof (ksi) min

Hardness

Nitronic 50

95

35

50

241

Nitronic 60

105

35

55

-

Grade

Mn

Si

P

S

Cr

Mo

SS416

0.15 max

1.25 max

1 max

0.06 max

0.15 min

Dec-14

0.6 max

SS440C

0.95

  - 1.20

1.00 max

1.00 max

0.040 max

0.030 max

16.00 - 18.00

-

SS446

0.20 max

1.50 max

0.75 max

0.040 max

0.030 max

23

-

Grade

Tensile

  Strength (MPa) min

Elongation

  (% in 50mm) min

Yield

  Strength 0.2% Proof (MPa) min

Hardness

Rockwell B (HR B) max

Brinell (HB) max

SS416

517

30

275

262

-

SS440C

1965

2

1896

-

-

STANDARD

WERKSTOFF NR.

UNS

JIS

BS

AFNOR

EN

SS416

1.4005

S41600

SUS 416

416S21

-

X12CrS13

SS440C

1.4125

S44004

SUS 440C

-

-

-

SS446

1.4762

S44600

SUS 446

446S21

-

X12Cr13

SS 416 Bright Bar Supplier

SS 416 Hex Bar Exporter in India

SS 416 Flat Bar

SS 416 Black Bar Stockists

ASTM A276 SS 416 Forged Round Bar

SS 416 Hot Rolled Round Bar

SS S41600 Round Bars Manufacturers

SS 416 Black Bar Stockholder

High Quality SS 416 Rods

Industrial SS 416 Rectangular Bars

SS 416 Square Bars Dealer in India

SS 416 Forged Bar Distributor in Mumbai

Standard

ASTM A276, ASTM A479

Dimensions

EN, DIN, JIS, ASTM, BS, ASME, AISI

Material Grade

Stainless Steel 439 (UNS S43035)

Stainless Steel 439 Bright Bars

Outside Diameter in the range of 4mm to 500mm

Stainless Steel 439 Bright Bars

Outside Diameter in the range of 4mm to 100mm

Stainless Steel 439 Hex Bars

18mm – 57mm (11/16″ to 2-3/4″)

Stainless Steel 439 Square Bars

18mm – 47mm (11/16″ to 1-3/4″)

Stainless Steel 439 Flats

1/2” to 10” in thickness range of 2mm to 150mm, Custom Size Stainless Steel Flats available

Length

1 to 6 Meters, Custom Cut Lengths

Form

Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc.

Finish

Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish

Grade

WERKSTOFF NR.

UNS

AFNOR

BS

JIS

SS 409

1.4512

S40900

Z3CT12

409 S 19

SUS 409

SS 409L

1.4512

S40903

–

–

SUS 409L

Grades

C

Ni

Si

S

Mn

P

Cr

Ti

SS 409

0.08

0.5

1.00

0.045

1.00

0.045

11.75 -10.5<

0.75-6x C

SS 409L

0.03

0.5

1.00

0.02

1.00

0.04

11.75-10.5

0.75-6(C+N)

SS 409M

0.03

1.00

0.5-1.5

10.80-12.50

1.5 max

0.040

0.030

0.03

Grades

Density

Melting Point

Tensile Strength

Yield Strength (0.2%Offset)

Elongation

Hardness (Brinell) MAX

Hardness (Rockwell B) MAX

SS 409

8.0 g/cm3

1457 °C (2650 °F)

Psi – 75000 , MPa – 515

Psi – 30000 , MPa – 205

35 %

Grade

WERKSTOFF NR.

UNS

AFNOR

BS

JIS

SS 409

1.4512

S40900

Z3CT12

409 S 19

SUS 409

SS 409L

1.4512

S40903

–

–

SUS 409L

SS 409M

–

S40920

–

HYFAB 3/12

SUS 409M

Grades

C

Ni

Si

S

Mn

P

Cr

Ti

SS 409

0.08

0.5

1.00

0.045

1.00

0.045

11.75 -10.5<

0.75-6x C

SS 409L

0.03

0.5

1.00

0.02

1.00

0.04

11.75-10.5

0.75-6(C+N)

SS 409M

0.03

1.00

0.5-1.5

10.80-12.50

1.5 max

0.040

0.030

0.03

Grades

Density

Melting Point

Tensile Strength

Yield Strength (0.2%Offset)

Elongation

Hardness (Brinell) MAX

Hardness (Rockwell B) MAX

SS 409

8.0 g/cm3

1457 °C (2650 °F)

Psi – 75000 , MPa – 515

Psi – 30000 , MPa – 205

35 %

SS 409L

8.0 g/cm3

1457 °C (2650 °F)

Psi – 75000 , MPa – 515

Psi – 30000 , MPa – 205

35 %

SS 439 HR Sheets

ASTM A240 Grade 409 / 409M / 409L / 410 / 430 / 430F / 431 / 439 / 441 Tread Plate

Specifications

ASTM A276, ASME SA276 / ASTM A479  ASME SA479

Dimensions

EN, DIN, JIS, ASTM, BS, ASME, AISI, ASTM, ASME

SS Round Bars

Outside Diameter in the range of 4mm to 500mm

SS Bright Bars

Outside Diameter in the range of 4mm to 100mm

SS Hex Bars

18mm – 57mm (11/16″ to 2-3/4″)

SS Square Bars

18mm – 47mm (11/16″ to 1-3/4″)

SS Flat Bars

1/2” to 10” in thickness range of 2mm to 150mm,

Finish

Black, Bright Polished, Rough Turned, Matt Finish, BA Finish

Length

1 to 6 Meters, Custom Cut Lengths

Wire Length

Max 12000 mm

Wire Diameter

5.5 – 400 mm

Form

Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc.

Grade

C

Mn

Si

P

S

Cr

Ni

420

0.15

max

1.00

max

1.00

max

0.04

max

0.03

max

min: 12.0

max: 14.0

-

420C

0.42 - 0.50

1.00

1.00 max

0.04

0.03

12.5 - 14.5

1.00 Max

Grade

Density

Melting Point

Tensile Strength

Yield Strength (0.2%Offset)

Hardness

Elongation

SS 420

8.0 g/cm3

1400 °C (2550 °F)

Psi – 95000 , MPa – 515

Psi – 50000 , MPa – 205

175

35 %

SS

420C

8.0 g/cm3

600°F (316°C)

1580

1365

444

14%

STANDARD

WERKSTOFF NR.

UNS

JIS

BS

GOST

AFNOR

EN

SS 420

1.4021

S42000

SUS 420 J1

420S29

-

-

FeMi35Cr20Cu4Mo2

SS 420C

1.4034

-

-

08Ch17N13M2T

Z44Cr13

X46Cr13

Product

Stainless Steel 904L Welded/ERW/Fabricated Pipes & Tubes

Standard Size

1/2″ NB to 16″ NB

ERW Type

1/2″ NB to 24″ NB

Fabricated (EFW Type)

6″ NB to 100″ NB

Unit Length

6 m, 12 m, 18 m, Custom Length

Thickness (mm)

0.8mm – 30 mm

Surface Finish

Anodized, Brushed, Mill Finished, Solution Annealed and Pickled, Polished Grit 120 – 600, Mirror Polished

Shape

Round, Square, Rectangular

Specification

ASTM A554, ASTM A312, ASTM A358 Class I to V, ASTM A249, ASTM A213, ASTM A268, ASTM A269, ASTM A789, ASTM A790

Type

Welded, Fabricated, ERW (Electrical Resistance Weld), LSAW Pipes

STANDARD

WERKSTOFF NR.

UNS

JIS

BS

EN

EURONORM NAME

SS 904L

1.4539

N08904

-

904S13

-

X1NiCrMoCuN25-20-5

Grade

C

Mn

Si

P

S

Cr

Mo

Ni

Cu

SS 904L

Min

-

-

-

-

-

19

4

23

1

Max

0.02

2

1

0.045

0.035

23

5

28

2

Grade

Tensile strength (MPa)

Yield Strength 0.2% Proof(MPa)

Elongation (% in 50mm)

Hardness - Brinell

904L

490

220

36

70-150

ASTM / ASME Name

ASTM A 358 / ASME SA 358 and ASTM A 312 / ASME SA 312

Most famous For

50 / 60 Nitronic Large Diameter Pipe

Dimensions Standard

ASTM, API, ASME

Nitronic 50 / 60 Seamless Pipes Size Range

1/2″ Nominal Bore To 16″Nominal Bore

OD Sizes

1/8" - 30″Nominal Bore Inch

efw pipes outer diameter

6″ Nominal Bore To 100″Nominal Bore

Available Pipes Form

Round and Hydraulic Form Etc

erw pipes Ranging in size from

1/2″ Nominal Bore To 24″ Nominal Bore

Nitronic 50 / 60 Seamless Pipes End Finishing

Theaded, Plain End, Beveled End

Frequently Used Type

ERW / Welded / LSAW/Fabricated Pipes

Pipes Schedule ThickneNitronic Range

SCH20, SCH40, SCH30, XS, STD, SCH80, SCH60, XXS, SCH80, SCH140 SCH160, SCH120,

Nitronic 50 / 60 Seamless Pipes Stock Length

Cut Length, Double and Single Random

STANDARD

WERKSTOFF NR.

UNS

Nitronic 50

1.3964

S20910

Nitronic 60

S21800

-

Grade

C

Mn

Si

P

S

Cr

Mo

Ni

Nitronic 50

0.06 max

4.0-6.0 max

1.00 max

0.045 max

0.030 max

23.5

3.00

13.5

Nitronic 60

min.

-

7.00

3.5

-

-

16.00

-

8.00

max.

0.10

9.00

4.5

-

-

18.00

0.75

9.00

Grade

Tensile Strength (ksi) min

Elongation (% in 50mm) min

Yield Strength 0.2% Proof (ksi) min

Hardness

Nitronic 50

95

35

50

241

Nitronic 60

105

35

55

-

Grade

C

Mn

Si

P

S

Cr

Mo

Ni

N

SS 321

0.08 max

2.0 max

1.0 max

0.045 max

0.030 max

17.00 – 19.00

0.10 max

9.00 – 12.00

5(C+N) – 0.70 max

SS 347

0.08 max

2.0 max

1.0 max

0.045 max

0.030 max

17.00 – 20.00

10xC – 1.10

9.00 – 13.00

62.74 min

Grade

Density

Melting Point

Tensile Strength

Yield Strength (0.2%Offset)

Elongation

SS 316

8.0 g/cm3

1457 °C (2650 °F)

Psi – 75000 , MPa – 515

Psi – 30000 , MPa – 205

35 %

SS 347

8.0 g/cm3

1454 °C (2650 °F)

Psi – 75000 , MPa – 515

Psi – 30000 , MPa – 205

35 %

STANDARD

WERKSTOFF NR.

UNS

JIS

BS

GOST

AFNOR

EN

SS 321

1.4541

S32100

SUS 321

-

–

-

X6CrNiTi18-10

SS 347

1.4550

S34700

SUS 347

–

08Ch18N12B

–

X6CrNiNb18-10

Stainless Steel 347H Welded Pipes Exporter in USA

347 Stainless Steel Welded Pipes Supplier in UAE

Stainless Steel 1.4550 Welded Pipes Supplier in Italy

S34700 Stainless Steel Welded Pipes Supplier in South Africa

Stainless Steel 1.4550 Welded Pipes

ASTM A312 TP347H Stainless Steel Welded Pipes

Stainless Steel TP 347 Welded Hollow Pipes

347H Stainless Steel Welded Pipes Supplier

A312 SS S34709 Welded Pipes Exporter in Egypt

Stainless Steel S34700 Welded Pipes Dealer

Grade

WERKSTOFF NR.

UNS

AFNOR

BS

JIS

SS 409

1.4512

S40900

Z3CT12

409 S 19

SUS 409

SS 409L

1.4512

S40903

–

–

SUS 409L

Grades

C

Ni

Si

S

Mn

P

Cr

Ti

SS 409

0.08

0.5

1.00

0.045

1.00

0.045

11.75 -10.5<

0.75-6x C

SS 409L

0.03

0.5

1.00

0.02

1.00

0.04

11.75-10.5

0.75-6(C+N)

SS 409M

0.03

1.00

0.5-1.5

10.80-12.50

1.5 max

0.040

0.030

0.03

SS 410

0.15 max

0.50 max

1.00

0.030

1.00

0.040

11.5 – 13.5

-

Grades

Density

Melting Point

Tensile Strength

Yield Strength (0.2%Offset)

Elongation

Hardness (Brinell) MAX

Hardness (Rockwell B) MAX

SS 409

8.0 g/cm3

1457 °C (2650 °F)

Psi – 75000 , MPa – 515

Psi – 30000 , MPa – 205

35 %

SS 409L

8.0 g/cm3

1457 °C (2650 °F)

Psi – 75000 , MPa – 515

Psi – 30000 , MPa – 205

35 %

SS 409M

8.0 g/cm3

1457 °C (2650 °F)

Psi – 75000 , MPa – 515

Psi – 30000 , MPa – 205

35 %

Grade

WERKSTOFF NR.

UNS

AFNOR

BS

JIS

SS 409

1.4512

S40900

Z3CT12

409 S 19

SUS 409

SS 409L

1.4512

S40903

–

–

SUS 409L

Grades

C

Ni

Si

S

Mn

P

Cr

Ti

SS 409

0.08

0.5

1.00

0.045

1.00

0.045

11.75 -10.5<

0.75-6x C

SS 409L

0.03

0.5

1.00

0.02

1.00

0.04

11.75-10.5

0.75-6(C+N)

SS 409M

0.03

1.00

0.5-1.5

10.80-12.50

1.5 max

0.040

0.030

0.03

SS 410

0.15 max

0.50 max

1.00

0.030

1.00

0.040

11.5 – 13.5

-

Grades

Density

Melting Point

Tensile Strength

Yield Strength (0.2%Offset)

Elongation

Hardness (Brinell) MAX

Hardness (Rockwell B) MAX

SS 409

8.0 g/cm3

1457 °C (2650 °F)

Psi – 75000 , MPa – 515

Psi – 30000 , MPa – 205

35 %

SS 409L

8.0 g/cm3

1457 °C (2650 °F)

Psi – 75000 , MPa – 515

Psi – 30000 , MPa – 205

35 %

SS 409M

8.0 g/cm3

1457 °C (2650 °F)

Psi – 75000 , MPa – 515

Psi – 30000 , MPa – 205

35 %

Grade

WERKSTOFF NR.

UNS

AFNOR

BS

JIS

SS 409

1.4512

S40900

Z3CT12

409 S 19

SUS 409

SS 409L

1.4512

S40903

–

–

SUS 409L

SS 409M

–

S40920

–

HYFAB 3/12

SUS 409M

Grades

C

Ni

Si

S

Mn

P

Cr

Ti

SS 409

0.08

0.5

1.00

0.045

1.00

0.045

11.75 -10.5<

0.75-6x C

SS 409L

0.03

0.5

1.00

0.02

1.00

0.04

11.75-10.5

0.75-6(C+N)

SS 409M

0.03

1.00

0.5-1.5

10.80-12.50

1.5 max

0.040

0.030

0.03

Grades

Density

Melting Point

Tensile Strength

Yield Strength (0.2%Offset)

Elongation

Hardness (Brinell) MAX

Hardness (Rockwell B) MAX

SS 409

8.0 g/cm3

1457 °C (2650 °F)

Psi – 75000 , MPa – 515

Psi – 30000 , MPa – 205

35 %

SS 409L

8.0 g/cm3

1457 °C (2650 °F)

Psi – 75000 , MPa – 515

Psi – 30000 , MPa – 205

35 %

SS 439 HR Sheets

ASTM A240 Grade 409 / 409M / 409L / 410 / 430 / 430F / 431 / 439 / 441 Tread Plate

Grade

WERKSTOFF NR.

UNS

AFNOR

BS

JIS

SS 409

1.4512

S40900

Z3CT12

409 S 19

SUS 409

SS 409L

1.4512

S40903

–

–

SUS 409L

SS 409M

–

S40920

–

HYFAB 3/12

SUS 409M

Grades

C

Ni

Si

S

Mn

P

Cr

Ti

SS 409

0.08

0.5

1.00

0.045

1.00

0.045

11.75 -10.5<

0.75-6x C

SS 409L

0.03

0.5

1.00

0.02

1.00

0.04

11.75-10.5

0.75-6(C+N)

SS 409M

0.03

1.00

0.5-1.5

10.80-12.50

1.5 max

0.040

0.030

0.03

Grades

Density

Melting Point

Tensile Strength

Yield Strength (0.2%Offset)

Elongation

Hardness (Brinell) MAX

Hardness (Rockwell B) MAX

SS 409

8.0 g/cm3

1457 °C (2650 °F)

Psi – 75000 , MPa – 515

Psi – 30000 , MPa – 205

35 %

SS 409L

8.0 g/cm3

1457 °C (2650 °F)

Psi – 75000 , MPa – 515

Psi – 30000 , MPa – 205

35 %

SS 439 HR Sheets

ASTM A240 Grade 409 / 409M / 409L / 410 / 430 / 430F / 431 / 439 / 441 Tread Plate